90 Degree Soft Lead-Free Flame Retardant Insulation PVC Compound for Cable Wire
Specifications PVC (Polyvinyl Chloride) is one of the most popular amorphous plastics. There are two kinds of PVC; one i
Send your inquiryDESCRIPTION
Basic Info
Material | Polyvinyl Chloride/PVC |
Usage | General Plastics |
Color | Red |
Density | 1.2-1.4G/Cm3 |
Ceretificate | Reach.RoHS |
Hardness | Shorea 60-85 |
Transport Package | Woven Bag |
Specification | 800*500*200 |
Trademark | Juli |
Origin | Zhejiang China |
HS Code | 3904220000 |
Production Capacity | 1000 Tons/Month |
Product Description
Specifications PVC (Polyvinyl Chloride) is one of the most popular amorphous plastics. There are two kinds of PVC; one is hard type and the other is flexible or soft.In the cable industry . Especially PVC having low temperature stability can easily stick to metallic surface when it's heated. PVC is widely used in cable industry because of its resistant for heavy weather condition, easy processing and better electrical properties.If PVC is directly subjected to heat, HCl (hydrogen chloride) is disseminated and colour of the PVC gets yellow. Depending on the rate of corruption due to the heat, color of PVC changes to yellow, red, brown, black respectively. During the heating, all physical and chemical properties change. During the process, toxic gases disseminate and humidity are got away by vacuum. Some additional materials should also be used in production process. These are generally as followings;PVC Formule1. PVC Resin
2. Plastiphians3. Stabilizetor4. Lubricant5. Filling (bedding) compound6. Strength modifier7. Compounds to facilitate of process8. PigmentsFlame retardant and optic bledcher material can also be used with above. Different type PVC granules can be produced by changing the rate of the above materials in the granule according to the requirements of application field for final product.PVC granules are mainly used as 2 different types in the cable industry as lifted below.
Technical specifications of 70 ºC pvc compound
Tensile Strength | MPa | 20.5 |
Fracture Tensile Strain | % | 320 |
Ageing Temperature | ºC | 100 |
Ageing Time | h | 168 |
Tensile Strength After Ageing | MPa | 22.5 |
Max Change of Tensile Strength | % | +12 |
After Ageing Fracture Tensile Strain | % | 290 |
Max Change of Fracture Tensile Strain | % | -10 |
Thermal Deformation | % | 28 |
Thermal Ageing Quality Loss | g/m² | 19 |
200ºC Thermal Stability Time | min | 90 |
20ºC Volume Resistivity | Ω.cm | 2.0*1011 |
Technical specifications of 90 ºC pvc compound
Tensile Strength | MPa | 20 |
Fracture Tensile Strain | % | 330 |
Ageing Temperature | ºC | 100 |
Ageing Time | h | 240 |
Tensile Strength After Ageing | MPa | 21.5 |
Max Change of Tensile Strength | % | +8 |
After Ageing Fracture Tensile Strain | % | 310 |
Max Change of Fracture Tensile Strain | % | -6 |
Thermal Deformation | % | 28 |
Thermal Ageing Quality Loss | g/m² | 9 |
200ºC Thermal Stability Time | min | 120 |
20ºC Volume Resistivity | Ω.cm | 2.0*1010 |
Our services:
1.Sales team can supply professional service with active attitude towards each question each requirement each issue.
2. 24 hours stand-by
3. Sample free ,but buyer need pay for freight cost
Sample:Free for the existed sample
Sample charge: 50-200usd depend on production, could be refunded after ordered
Sample production time: 5-7 days
Shipping fee: prepaid or collect
Related Products
-
Hot Style Lightweight Eco-Friendly PVC Granules for Cable and Wire
-
BS 7655 Aoi 28% Flame Retardant Flexible PVC Compound 80A for Cable Insulation
-
Polyvinyl Chloride Rigid Compounds Granules for Printed PVC Heat Shrink Film
-
Factory Directly Sales Transparent PVC Compound Granule for Shoes Soles/Clear Crystal Rain Boots/Sandles